Monolayer colloidal aqueous solution Ti2C MXenes
| 【Numbering】BK2021032002 | 【CAS】12316-56-2 | ||
| 【Item No.】BK2021032002-04 | 【specification】 | ||
|
|||
Name: Single-layer colloidal solution Ti2CTx MXenes
Functional group: -OH-F-O-Cl (customizable)
Size: less than 500nm less than 200nm less than 100nm less than 50nm
Purity: 99%
Storage conditions: low temperature, dry and sealed, must be stored in an inert atmosphere
Process: HF treatment or HCl+LiF treatment
|
MXenes材料 MXenes material |
|||
|
|
名称 Product name |
工艺 Processing technology |
具体细节 Details |
|
Ti2C |
风琴状 Organoid material |
HF处理 HF Treatment |
风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF. |
|
单/少层粉末材料 Single/Layer Powder Material |
冷冻处理 cryogenic treatment |
单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
|
|
|
Nb2C |
风琴状 Organoid material |
HF处理 HF Treatment |
风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF. |
|
单/少层粉末材料 Single/Layer Powder Material |
冷冻处理 Cryogenic treatment |
单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
|
|
|
V2C |
风琴状 Organoid material |
HF处理 HF Treatment |
风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF. |
|
单/少层粉末材料 Single/Layer Powder Material
|
冷冻处理 cryogenic treatment |
单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
|
|
|
Ti3C2 |
风琴状 Organoid material |
HF处理 HF Treatment |
风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF. |
|
黏土材料 Clay materials |
LiF处理 LiF Treatment |
黏土材料，经超声离心可分散为单层材料，产率约为25-35%。超声功率需160W以上，时间约为2h到6h。 Clay material, which can be dispersed as a single layer material by ultrasonic centrifugation, yields about 25-35%. Ultrasound power needs more than 160W, and the time is about 2 h to 6 h.
|
|
|
单/少层胶体溶液 Single/Layer Colloidal Solution
|
5mg/ml 100ml |
单/少层村料的胶体溶液，具有丁达尔现象，可以直接利用的MXenes材料。 The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.
|
|
|
单/少层胶体溶液 Single/Layer Colloidal Solution
|
10mg/ml 100ml |
单/少层村料的胶体溶液，具有丁达尔现象，可以直接利用的MXenes材料。 The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly. |
|
|
单/少层粉末材料 Single/Layer Powder Material |
freeze drying |
单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。 Powder obtained by freeze-drying of colloidal solution of single/small layer village material. |
|
|
自支撑膜材料 Self-supporting membrane materials |
真空抽滤 Vacuum suction filtration
|
单/少层村料的胶体溶液，经过真空抽滤得到的柔性膜。Flexible membranes obtained from the colloidal solution of single/small-layer village materials by vacuum filtration. |
|
具体表征请见附件：MXene手册
| Warm tips: Suzhou Beike nano products are only used for scientific research, not for human body,different batches of products have different specifications and performance |
Message
|
| Warm tips: Suzhou Beike nano products are only used for scientific research, not for human body,different batches of products have different specifications and performance.The website pictures are from the Internet. The pictures are for reference only. Please take the real object as the standard. In case of infringement, please contact us to delete them immediately. |
Previous： the end...
Next： Porous monolayer MO2C